Fracture Grade Organoclay Rheological Additive , Rapid High Yield Paint Thickener

Organoclay fracture grade

Organoclay fracture grade Self activating with highly effective and rapid high yield in mineral oil based

Organoclay CP-34 is an organophilic clay (modified bentonite), designed especially for use in solvent based system. It can be used widely in solvents from low polarity to medium-high polarity. Rheological additive furnish the drilling mud(fluid) with good suspension,wall-protection and anti-filtration properties.No need for polar activator in oil drilling application and maintain stable physical performance under the pressure of 108 at the temperature of 230ºC.

   1, Properties

Composition Organic derivative of a montmorillonite clay

Appearance Fine powder, light yellow

Moisture content (105℃,2hr) ≤3.5%

Loss on ignition (1000℃) 28%-30%

Bulk density 0.53g/cm3

Fineness (<74μm, %) ≥98%

2, Advantages

  • High gelling efficiency
  • Light color gel
  • Produce reproducible thixotropic consistency over a wide temperature range
  • Imparts particle suspension, preventing hard settling of pigment and fillers.
  • Exerts strong film reinforcing action in organic binder systems.

3, Organoclay-fracture-grade CP-34 is used in the following applications:

  • Marine paint, Industrial paint, heavy-duty, anticorrosion paint such as bituminous coatings, polyester paints, Alkyd paints.
  • Sealant
  • Inks
  • Grease
  • Unsaturated polyester putty
Chemical ingredient Alkyl Quaternary Ammonium bentonite Quartz(SiO2)
CAS. No. 68953-58-2 14808-60-7
Content >99% <1%
Item Standard Result
Appearance Fine powder, light white Fine powder, light white
Moisture Content(105, 2hr) 3.5% 2.5%
Viscosity, mpa(20-25) 900 4800
Fineness(<0.074mm) 98% 99.8%

4, Using

CP-34 disperses under high shear and requires a polar activator for best efficiency. Heat is not required to obtain good dispersion. Addition levels are typically in 0.2%~2.0%. Polar activator (95% Ethanol or 95% Methanol) is needed. Normally addition level of polar activator is recommended to be 40%~50% of CP-34 in weight. If in xylene system, addition level of polar activator is about 30%-40% of CP-34 in weight.

Pre-gel is made as below procedure.

  • Charge solvent to mill
  • Slowly add CP-34(6-10% by weight of total pregel) to mill under agitation.
  • Mix at high speed for 5 minutes.
  • Add polar activator.
  • Mix at high speed for 5 minutes.

All safety information is provided in the Material Safety Data Sheets for Zhejiang Camp-Shinning New Material Co.,Ltd..

Package

Kraft paper bag with PE liner or multi-wall paper sacks or customized. 25kg/bag or 22.68kg/bag or customized

Storage

CP-34 has a shelf life of 2 years, and should be stored in ventilated cool and dry place.

            Notice

The information on use is based on data which are believed reliable, but any recommendation or suggestion made is without guarantee or warranty, since the conditions of use are outside our control. All products are sold on the conditions that purchasers shall make their own tests to determine the suitability of such products for their purpose and that all risks are assumed by user. We disclaim any responsibility for damages resulting from careless or improper handling or use. Nothing herein is to be taken as permission, inducement or recommendation to practice any patented invention without a license.