Thixotropic agent Properties
Composition Organic derivative of a montmorillonite clay
Appearance Fine powder, white
Moisture content (105℃,2hr) ≤3.5%
Loss on ignition (1000℃) 40%-44%
Bulk density 0.40~0.60g/cm3
Fineness (<74μm, %) ≥99.8%
Dispersion fineness (μm) ≤10
High purity, low silica content.
Easy dispersing, fine particle size. Easy to use, no need to pregel
High viscosity and high thixotropic.
Wide application range. It can be applied in almost all resins and solvents
Gel is very transparent and of light color.
Paints including top grades paint, decorative paint, industrial paint, traffic paint etc.is used in the following applications:
Oil Drilling Mud
1. Pre-gel method
A. Polar activator is not necessary:
a. Main solvent xylene: 95~92%
b. Rheology organoclay CP-720B:5~8%
c. Dispersing 5-15min, gel is finished.
B. Polar activator is necessary:
a. In aromatic solvent, the recommend activator is methyl acohol/water (95%/5%)/ acolhol/water (95%/5%), the dosage is 33%-45% based on the weight of thixotropic clay.
2. Procedure of adding gel:b. In mineral oil (such as 200#), white oil, diesel oil, the recommend activator is methyl acohol/water (95%/5%)/acolhol/water(95%/5%), the dosage is 33%-60% based on the weight of thixotropic clay.
A. Charge solvent and resin to mill
B. Slowly add the gel
C. Dispersing 5-10min
D. Wetting agent (if required)
E. Disperse completely to desired fineness
F. Dilute to desired viscosity
3. Add directly with powder
A. Charge solvent and resin
B. Add Organo bentonite CP-720B slowly
C. Disperse 10-15min
D .Add polar activator (if necessary)
E. Disperse 10-15min at high speed
F. Add wetting agent and other additive
G. Grind and next procedure
Thixotropic additive can be added directly in powder under high shear condition. The addition is recommended to be before grinding procedure to get the best effectiveness. Addition level is commonly 0.1%~2.0%. If add polar activator and make pre-gel, better efficiency can be achieved.